Korrosionsschutz mit Beschriftungsfeld enHere is an overview of our   1c hydro small   systems

  • Primer

    article product name product description
    HV 186 (FL) CHING-HYDROVERSAL-primer Quick drying, water based AY-primer with active corrosion protection for steel, galvanized steel and non-ferrous metals
    Film thickness: 60-80 µm
    HV 185 EPD (FL) CHING-HYDROVERSAL-primer on EPD Special water based AY-primer with active corrosion protection for EPD coated steel(2) but also as a direct coating for steel, zinc and aluminium; quick drying
    Film thickness: 60-80 µm
    HV 286 EPD (FL) CHING-HYDROVERSAL-primer on EPD Special water based AY-primer for EPD coated steel(2); quick drying
    Film thickness: 60-80 µm
    WS 181 CHING-HYDRO-weld primer Water based AY-weld primer with active corrosion protection for steel; quick drying
    Film thickness: 15-25 µm
    HR 126 CHING-HYDRO-transport coating «temporary corrosion protection» Water based AY-primer for temporary corrosion protection of steel; so-called «transport coating»
    Film thickness: 40-60 µm / 80-100 µm
    HVS 186 CHING-HYDROVERSAL-primer Quick drying, water based AY-primer with active corrosion protection for steel and galvanized steel with or without pre-existing coating
    Film thickness: 60-100 µm
    HVS 186 K CHING-HYDROVERSAL-primer «surface-tolerant» Quick drying, water based AY-primer with active corrosion protection for steel with or without pre-existing coating; surface tolerant also for manually derusted steel prepared to St 2-3
    Film thickness: 60-80 µm
    HVS 03 CHING-HYDROVERSAL-MICA-primer Quick drying, water based AY-primer with MICA and active corrosion protection for galvanized steel; initial on-site coating
    Film thickness: 60-80 µm
    HVSP 03 CHING-HYDROVERSAL-MICA-primer Quick drying, water based AY-primer with MICA and active corrosion protection for galvanized steel; factory coating
    Film thickness: 60-80 µm
  • Intermediate Coats

    article product name product description
    HV 33 (FL)
    HV 30 (FL)
    CHING-HYDROVERSAL-intermediate coating Quick drying, water based AY-intermediate coating with barrier effect for passive corrosion protection
    Optional: MICA-pigmenting or iron mica-pigmenting
    Film thickness: 80-100 µm
  • Top Coats

    article product name product description
    HV 47 (FL)
    HV 43 (FL)
    HV 40 (FL)
    CHING-HYDROVERSAL-top coating Quick drying, water based AY-top coating with high weathering resistance
    Gloss level: matt to glossy
    Optional: MICA-pigmenting or iron mica-pigmenting
    Film thickness: 60-80 µm
  • Single Layer

    article product name product description
    HV 08 (FL)
    HV 03 (FL)
    CHING-HYDROVERSAL-single coat paint Quick drying, water based AY-single coat paint with active corrosion protection for steel, galvanized steel and non-ferrous metals; high weather resistance
    Gloss level: matt to semi-gloss
    Optional: MICA pigmenting
    Film thickness: 60-80 µm
    HVS 03 CHING-HYDROVERSAL-MICA-single coat paint Quick drying, water based AY-top coating or single coat paint with MICA for primed steel and primed galvanized steel; high weather resistance; also suitable as direct coating on galvanized steel; as initial on-site coating
    Film thickness: 60-120 µm
    HVSP 03 CHING-HYDROVERSAL-MICA-single coat paint Quick drying, water based AY-single coat paint with MICA for galvanized steel; high weather resistance; factory coating
    Film thickness: 80-120 µm
    HVT 00 CHING-HYDROVERSAL-iron mica-single coat paint Quick drying, water based AY-single coat paint with iron mica for galvanized steel; high weather resistance; factory coating
    Film thickness: 80-120 µm

Overview binders

AK alkyd resin ESI ethyl silicate resin PVC/AK polyvinyl chloride/alkyd resin-combination
AY acrylic resin PAS polyaspartic PVC/AY polyvinyl chloride/acrylic resin-combination
AK/AY alkyd resin/acrylic resin-combination PES polyester resin SI silicone resin
EP epoxy resin PUR polyurethane resin      
EPE epoxy resin ester PVB polyvinyl butyral resin