Here is an overview of our1c solvent smallsystems

  • Primer

    article product name product description
    FS 182 CHING-FIX-weld primer AK-weld primer with active corrosion protection for steel; dries quickly
    Film thickness: 15-25 µm
    FSS 186 CHING-FIX-quick primer AK-resin primer with active corrosion protection for steel; dries quickly
    Film thickness: 40-60 µm
    FSD 186 CHING-FIX-primer AK-primer with active corrosion protection for steel; dries quickly
    Film thickness: 60-80 µm
    BS 182 CHING-high-solid-primer High-solid-AK-primer with active corrosion protection for steel; after drying recoating with 2-comp. EP or 2-comp. PUR coating products possible
    Film thickness: 40-60 µm
    BS 1082 CHING-high-solid-primer «surface-tolerant» High-solid-AK-primer with active corrosion protection for steel; after drying recoating with 2-comp. EP or 2-comp. PUR coating products possible; surface-tolerant also on manually derusted surfaces St 2-3
    Film thickness: 40-60 µm
    R 126 CHING-transport coating «temporary corrosion protection» AK-/AY-Primer for temporary corrosion protection of steel; so-called "transport coating"
    Film thickness: 40-60 µm / 80-100 µm
    ED 152 CHING-EPE-zinc dust-primer EPE-zinc dust primer with cathodic corrosion protection for blasted steel; zinc content ≥ 94 % [Zn (R)]; temperature-resistant up to 150 °C
    Film thickness: 80-100 µm
    ED 182 CHING-EPE-primer EPE-Primer with active corrosion protection for steel and grey iron; resistant to hydraulic oils
    Film thickness: 60-80 µm
    PV 124 CHING-PVB-primer Quick drying PVB-primer for steel, galvanized steel and non-ferrous metals; universally recoatable with all commercially available 1-comp. and 2-comp. paints
    Film thickness: 10-20 µm / 30-40 µm
    SI 152 CHING-silicone-primer SI-Zinc dust primer with cathodic corrosion protection for blasted steel (zinc content: ≥ 94 %); temperature-resistant up to 600 °C; mechanical note: stress resistance is only achieved after "stoving" of approx. 1 hour at 230-250 °C.
    Film thickness: 30-40 µm
    ESI 152 CHING-ESI-zinkum ESI-zinc dust primer with cathodic corrosion protection for blasted steel; zinc content ≥ 94 % [Zn (R)]; temperature-resistant up to 400 °C
    Film thickness: 40-80 µm
    TSD 186 CHING-TEX-S-primer PVC/AK-primer with active corrosion protection for superior corrosion protection on steel
    Film thickness: 80-100 µm
    SFC 182 CHING-ALVITE-COLOR-primer PVC/AY-Primer with active corrosion protection for steel and non-ferrous metals; on galvanized steel for superior duplex systems
    Film thickness: 80-100 µm
    SFC 1082 CHING-ALVITE-COLOR-primer «surface-tolerant» PVC/AY-Primer with active corrosion protection for steel, galvanized steel and non-ferrous metals; surface tolerant also on manually derusted surfaces St 2-3
    Film thickness: 80-100 µm
    SAD 182 CHING-SuprAlvite-primer Low-solvent primer on special polymer resin basis with active corrosion protection for steel with or without pre-existing coating; surface tolerant also for manually derusted steel prepared to St 2-3; cost-effective
    Film thickness: 60-80 µm
    SAD 182 P CHING-SuprAlvite-primer «surface-tolerant» Quick drying, low-solvent primer on special polymer resin basis with active corrosion protection for steel and galvanized steel with or without pre-existing coating; surface tolerant also on manually derusted steel prepared to St 2-3
    Film thickness: 60-80 µm
    SAD 00 P CHING-SuprAlvite-primer Quick drying, low-solvent iron mica primer on special polymer resin basis with active corrosion protection for galvanized steel; as on-site initial coating or factory coating
    Film thickness: 80-120 µm
    SAD 182 SHS M CHING-SuprAlvite-high-solid-primer «surface-tolerant» Zinc-free high-solid primer on special polymer resin basis for steel and galvanized steel with or without pre-existing coating; surface tolerant also for manually derusted steel prepared to St 2-3
    Film thickness: 60-80 µm
    KT 008 CHING-contact primer Diffusion-resistant sealing primer with good penetration properties and with active corrosion protection for slowly corrosive steel (COR-TEN steel)
    Film thickness: 10-20 µm
  • Top Coats

    article product name product description
    FSS 47 CHING-RAPID-top coating AK-top coating; quick drying
    Gloss level: satin gloss to high gloss
    Film thickness: 40 µm
    FSD 47
    FSD 40    		 CHING-FIX-top coating AK-top coating; quick drying
    Gloss level: satin gloss to high gloss
    Optional: iron mica-pigmenting
    Film thickness: 80 µm
    SI 45
    SI 40    		 CHING-silicone-top coating SI-top coating on silicone resin basis with aluminium pigment; temperature-resistant up to 600° C
    Film thickness: 25 µm
    Optional: iron mica-pigmenting; temperature-resistant up to 400° C
    Film thickness: 40 µm
    Note: The mechanical stress resistance is only achieved after «stoving» for approx. 1 h at 230-250 °C
    SFC 07
    SFC 00    		 CHING-ALVITE-COLOR-top coating PVC/AY-top coating or -single coat paint with direct adhesion on steel and non-ferrous metals; on galvanized steel for superior duplex systems
    Gloss level: semi-gloss
    Optional: iron mica-pigmenting
    Film thickness: 80-100 µm
    SAD 00 P
    SAD 06 P    		 CHING-SuprAlvite-top coating Quick drying, low-solvent, iron mica top coating or single coat paint on the basis of special polymer resin for primed steel and primed galvanized steel; also suitable as direct coating on galvanized steel; as initial on-site coating or factory coating
    Optional: MICA-pigmenting
    Film thickness: 80-120 µm
    SAD 00
    SHS M    		 CHING-SuprAlvite-high-solid-top coating High-solid iron mica top coating on a special polymer resin basis for primed steel and primed galvanized steel
    Film thickness: 80-100 µm
  • Single Layer

    article product name product description
    FSD 08
    FSD 06    		 CHING-FIX-single coat paint AK-single coat paint with active corrosion protection for steel; quick drying
    Gloss level: matt to satin gloss
    Optional: MICA-pigmenting
    Film thickness: 80 µm
    SAD 00
    SHS E M    		 CHING-SuprAlvite-high-solid-single coat paint High-solid-iron mica single coat paint on special polymer resin basis for direct coating on galvanized steel
    Film thickness: 80-100 µm

Overview binders

AK → alkyd resin ESI → ethyl silicate resin PVC/AK → polyvinyl chloride/alkyd resin-combination
AY → acrylic resin PAS → polyaspartic PVC/AY → polyvinyl chloride/acrylic resin-combination
AK/AY → alkyd resin/acrylic resin-combination PES → polyester resin SI → silicone resin
EP → epoxy resin PUR → polyurethane resin      
EPE → epoxy resin ester PVB → polyvinyl butyral resin